Ⅰ. Description
A molded product that is incomplete because the mold cavity was not filled completely.
Ⅱ. Causes
Insufficient injection-molding machine performance (shot capacity, plasticizing capacity, etc.)
Poor material flowability
Gate cross-section surface area is too small. Molded product thickness is too thin.
Poor gas venting.
Ⅲ. Countermeasures
<Molding equipment>
Increase the amount of material feed. If material feed is still insufficient at maximum material feed capacity, change to a larger capacity machine.
Install a screw with a back-flow check valve.
Increase injection pressure
Raise the cylinder temperature setting. Raise the nozzle temperature, too.
Make sure there are no severed lines to the heater.
Make sure the nozzle is not clogged. If the nozzle clogs frequently, raise the mold temperature or shorten the cycle time.
Increase injection speed
<Mold>
Raise the mold temperature.
Increase the mold gas release.
Increase gate cross section surface area.
Increase the molded product thickness.
Add ribs to the molded product design to improve flowability.
<Materials>
Choose a low-viscosity high flow material type.
Apply surface lubricant. (Add 0.05-0.1% by weight.)
Flow marks

Ⅰ. Description
Ring shaped miniature bands appear on the molded product surface around gates or narrow sections.
Ⅱ. Causes
The molten polymer cools rapidly within the mold and becomes highly viscous. Once that molten polymer starts to coagulate, it gets pushed by the molten polymer injected afterward and forms miniature bands.
Ⅲ. Countermeasures
<Molding equipment>
Increase the nozzle diameter. Increase the nozzle temperature
Increase injection speed.
Increase injection pressure.
Raise the cylinder temperature.
Reduce the cushion. (Reduce the charging amount.)
<Mold>
Increase the mold temperature.
Provide a cold slug well.
Increase the gate cross section surface area.
Create more distance between the gates and the location of the mold coolant.
<Materials>
Apply surface lubricant.
Silver streaking

Ⅰ. Description
Streaks of a silvery white color appear in the material flow direction.
Ⅱ. Causes
Material is absorbing water.
Material is contaminated with another type of material.
Aeration is occurring during molding.
Too much additive is present.
Ⅲ. Countermeasures
<Molding equipment>
Apply back pressure to generate a kneading effect.
Slow down injection speed.
Thoroughly clean molding machine cylinders.
<Mold>
Increase (or decrease) the size of the runners and gates.
Increase the mold temperature.
Change the gate locations.
<Materials>
Pre-dry thoroughly.
Install an ultrared light inside the hopper.
Investigate for potential contamination.
Poor weld line

Ⅰ. Description
The material splits off and flows in two or more directions. When the divergent flow fronts converge again, hair-like lines appear where they meet. This results in reduced strength, as well as burn-mark and bubble defects.
Ⅱ. Causes
Material splits and flows in separate directions, then converges again.
Polymer temperature is too low. Polymer is not fully melted.
Difficulties in venting gas and air.
Ⅲ. Countermeasures
<Molding equipment>
Raise the resin temperature
Increase the injection pressure.
Increase the injection speed.
<Mold>
Provide a cold slug well where weld lines occur.
Provide a gas vent.
Change the gate locations. Or increase the number of gates.
Stop using mold parting agents.
Change the gate locations so that the weldlines occur in locations less susceptible to external forces if weld strength is an issue.
<Materials>
Choose a low-viscosity high flow type material.
Voids

Ⅰ. Description
The presence of holes inside molded products
Ⅱ. Causes
Change in density as the material changes from a molten to a coagulated state.
The surface of the molded product loses heat rapidly through the mold wall and the polymer hardens. As a result, the polymer is pulled outward, causing all shrinkage to concentrate in the thickest parts of the product leaving holes within the product. In molded products with a thickness greater than 6 mm, voids are very difficult to avoid.
Air gets trapped within the molten polymer, leaving bubbles within the product
Ⅲ. Countermeasures
<Molding equipment>
Increase the injection pressure. (Increase the secondary pressure, too.)
Extend the injection time.
Lower the cylinder temperature setting.
<Mold>
Change the product design so that the thickness is no greater than 6 mm. To enhance strength, add several thick, uniform reinforcement ribs to the product design. Avoid thickness where possible.
Increase the size of the fates. Enable supplemental re-filling.
Make the runners shorter.
Lower the mold temperature. Make the mold temperature uniform.
Change the gate locations so as to prevent air intake.
<Materials>
Dry the material thoroughly.
Choose a highly viscous grade.
Sink marks

Ⅰ. Description
The surface of the molded product collapses somewhat-something that is particularly common in thicker products.
Ⅱ. Causes
Same as what causes voids, but sink marks arise when the surface cools too slowly.
Ⅲ. Countermeasures
<Molding equipment>
Increase the amount of material feed.
Increase the cavity internal pressure (secondary pressure).
Lower the cylinder temperature setting.
Increase the injection rate.
Increase the injection speed.
Lengthen the injection time.
<Mold>
Lower the mold temperature.
Make the mold temperature uniform.
Change the gate locations.
Make the gates larger.
Make the runners shorter.
<Materials>
Choose a highly viscous grade.
Warpage

Ⅰ. Description
The molded product warps immediately following or at some time following molding where the mold cavity should be straight.
Ⅱ. Causes
Residual stress from the molding process is released, causing deformation.
Ⅲ. Countermeasures
<Molding equipment>
Decrease the injection pressure.
Lower the cylinder temperature setting.
Lengthen the cooling time.
<Mold>
Make the thickness of the molded product uniform.
Eliminate undercuts.
Operate the knock out pins in a uniform fashion.
Provide multiple knock out pins.
Change the gate locations.
Lower the mold temperature.
Screw engagement failures

Ⅰ. Description
When feeding material for measurement, the screw rotates but does not engage the screw thread, or the screw does not turn at all.
Ⅱ. Causes
Occurs when the coefficient of friction between the material and another material, the material and the screw, or the material and the heating cylinder is unusually low or unusually high.
Ⅲ. Countermeasures
<Molding equipment>
Install a screw equipped with a back-flow check valve.
Choose a short compression type screw.
Change the cylinder temperature setting. Lower if the screw turns without engaging, raise if the screw is not turning.
Check to make sure no lines to the cylinder heater have been severed.
Perform an empty shot at least five times.
<Materials>
Apply a surface lubricant.
Make the granularity of the material uniform.
Sticking of parts in the mold

Ⅰ. Description
Ordinarily a molded product is removed from the mold by having the product stick to the moving side of the mold when the mold opens, after which the product is ejected using ejector pins. Sticking occurs when the part fails to separate from the stationary mold or from the moving mold. In the case of the latter, the problem could result in broken ejector pins.
Ⅱ. Causes
Possible causes include: the mold draft is too small; there is too much residual pressure from the molding process; too much shrinkage occurred; or the mold finish is perpendicular to the part release direction.
Ⅲ. Countermeasures
<Molding equipment>
Decrease injection pressure.
Lower the cylinder temperature setting.
<Mold>
Increase the mold draft.
Improve the mold finish.
Eliminate undercuts.
Use a more appropriate mold temperature. Be mindful of that fact that, in the case of box-shaped parts, the part will likely stick to the stationary mold if the stationary mold temperature is low.
Apply a mold parting agent.
Burn marks

Ⅰ. Description
Discoloration or dark reddish brown streaks in the molded product.
Ⅱ. Causes
Heat decomposition of the material.
Ⅲ. Countermeasures
<Molding equipment>
Lower the cylinder temperature setting.
Shorten the intermediate time (dry cycle time).
The ram is recessed for too long of a time duration.
Slow down injection speed.
<Mold>
Provide a larger gas vent.
Increase the gate sizes.
Reply

Important Note..!

If you are not satisfied with above reply ,..Please

ASK HERE

So that we will collect data for you and will made reply to the request....OR try below "QUICK REPLY" box to add a reply to this page
Popular Searches: plastic components molding defects ppt, seminars on injection molded plastic for mechanical engg, plastic injection beads, free download aws welding defects ppt, defects in pharmaceutical packaging pdf, welding defects ppt free download, general injection moulding ppt,

[-]
Quick Reply
Message
Type your reply to this message here.

Image Verification
Please enter the text contained within the image into the text box below it. This process is used to prevent automated spam bots.
Image Verification
(case insensitive)

Possibly Related Threads...
Thread Author Replies Views Last Post
  pdf k53 learners test questions and answers 2015 pdf 2 11,126 18-05-2018, 06:21 PM
Last Post: Guest
  soil stabilization using plastic ppt download Anand a. M 2 1,879 20-11-2017, 08:50 PM
Last Post: perfect dreamer
  pdf anchoring script in english pdf 2 1,776 21-07-2016, 12:49 PM
Last Post: jaseela123d
  the state of anti plastic campaign the laws its effects and implementation in india 1 1,826 26-05-2016, 12:19 PM
Last Post: dhanabhagya
  the state of anti plastic campaign the laws its effects and implementation wikipedia 1 2,100 25-05-2016, 01:31 PM
Last Post: dhanabhagya
  pdf of any book of jelet exam pdf file 1 1,545 23-05-2016, 11:36 AM
Last Post: dhanabhagya
  infrared plastic solar cell seminars report 1 726 13-05-2016, 10:14 AM
Last Post: dhanabhagya
Wink silicon on plastic ppt 1 564 12-05-2016, 11:01 AM
Last Post: dhanabhagya
Question seminar report on plastic roads pdf 1 1,253 26-04-2016, 09:18 AM
Last Post: dhanabhagya
  fuel from plastic waste pdf 1 775 25-04-2016, 01:02 PM
Last Post: dhanabhagya

Forum Jump: